镀铝镁锌是近年来研发的一种板材，主要为了取代不锈钢产品和提高镀锌板的性能。在其板材中添加了合适比例的锌、铝、镁，使其产生复合效果，具有高强度的抗腐蚀性，是一种高耐腐蚀性的新型环保型钢板。它在严酷的腐蚀环境下仍然保持钢板的原来面貌，减少了一般刚才后期加工工艺，降低了使用后续成本，同时减少了电镀，该产品节约了资源也保护了环境，而佛山万庆物资钢铁的镀铝镁锌板采用全新环保铝，安全无甲醛，严格通过环境管理体系认证，可回收利用，而且产品品质稳定，20年品质如一，结实耐用达到钢材检测规定厚度，不易变形。

Aluminized magnesium zinc is a plate developed in recent years, mainly to replace stainless steel products and improve the performance of the galvanized plate.An appropriate proportion of zinc, aluminum, magnesium is added to its plate, so that it produces a composite effect, with high strength corrosion resistance, which is a new environmental protection steel plate with high corrosion resistance.It still remains in the harsh corrosion environment of the original appearance, reduce the general post processing process, reduce the subsequent cost, reduce the electroplating at the same time, the steel product saves resources also protect the environment, and aluminum environmental protection aluminum, safety without formaldehyde, strictly through the environmental management system certification, recycling, and stable product quality, 20 years of quality, durable to steel detection thickness, not easy to deformation.

许多板材贸易公司都提供折弯加工服务，在折弯这道工序时，一般的材料防腐能力下降易生锈，而佛山万庆物资的镀铝镁锌镀层其延展性很好，在折弯工序中折弯处的镀层不被破坏，因此折弯处的防腐性能不会下降。在冲孔、剪切等工序，由于镀铝镁锌管切割面部分基地外漏，初期会产生红锈，但随后切割端口周围的镀膜开始溶解，形成以氢氧化锌碱性氯化锌以及氢氧化镁等主要成分的致密保护膜，这一过程持续一段时间后，切割部分将被完全覆盖（恢复保护性能），该保护膜导电性能较弱，可以抑制端口部分的腐蚀反应，并且镀膜中所含的硅还有促成这一保护膜形成的作用。

Many plate trading companies provide bending processing services. In the bending process, the general material corrosion resistance is easy to rust, while the aluminum plated magnesium zinc coating of Foshan Wanqing materials is very good, and the coating at the bending process is not damaged in the bending process, so the anti-corrosion performance at the bending process will not decrease.In the punching, cutting and other processes, due to the leakage of the base, but then the coating around the cutting port of red rust began to dissolve, forming a dense protective film with zinc hydroxide alkaline zinc hydroxide and magnesium hydroxide and other main components of the process, this cutting part will last for a period of time, the process will be fully covered (restore the protective performance), the protective film conductivity is weak, can inhibit the corrosion reaction of the port part, and the silicon contained in the coating also contribute to the formation of the protective film.